Specifications

 

 

4. The HGM - A high friction composition brake shoe steel back and friction body two parts.

Brake shoe shape size (mm) :

(1) the steel back of outer arc: R450

(2) brake shoe width: 820-1

(3) the thickness of the brake shoe: 45

 

5. The steel back is made of Q235A steel manufacturing, steel plate performance shall comply with the provisions of GB/T700.

 

6. Brake shoe is made up of steel back and friction.Friction main raw material for: phenolic resin, nitrile rubber, steel fiber,

reduced iron powder, graphite, etc.

 

7. The friction performance component of the learning performance and friction wear performance of two parts.

 

The mechanical properties shall comply with:

Table 1 physical and mechanical performance of the brake shoe

 

Unit performance indicators

G/cm3 density less than nominal worth plus or minus 5%

The compression strength of 25 Mpa or greater

The impact strength acuity 2.0 kJ/m2

The compression modulus of Mpa to 1.3 * 103 or less

Rockwell hardness (HRR) 90 or less

Water absorption percentage < 1.5%

Oil absorption percentage < 1.5%

 

Brake friction wear performance should be consistent with:

Table 2.The change of the instantaneous friction coefficient range (20 kn brake shoe pressure)

Speed (km/h) 0 10 20 30 to 40 50 to 60

The maximum 0.63 0.602 0.558 0.546 0.515 0.482 0.471

Standard 0.48 0.46 0.43 0.42 0.39 0.37 0.36

The minimum 0.42 0.40 0.40 0.36 0.33 0.32 0.37

Nylon PA

Nylon PA, also known as polyamide, is a synthetic polymer that is widely used in various industries. It was first developed in the 1930s by a team of scientists led by Wallace Carothers at DuPont. Nylon PA was the first synthetic fiber to be produced commercially and has since become a popular material due to its durability, strength, and versatility.
Nylon PA is made by combining two monomers, hexamethylenediamine and adipic acid, through a process called condensation polymerization. The resulting polymer has a high molecular weight, which gives it its strength and durability. Nylon PA is a thermoplastic material, which means it can be melted and molded into various shapes and forms.
One of the most notable properties of Nylon PA is its high tensile strength. It can withstand a lot of stress without breaking, making it ideal for use in applications that require strong materials. Nylon PA is also resistant to abrasion, chemicals, and UV radiation, which makes it suitable for use in harsh environments.

Nylon Pa,Plastic Parts Mold,Nylon Carbon Fiber Pa,Plastic Part Mold

Rayhot Technology Group Co,.Ltd , https://www.rayhotgroup.com